VMWP02500 | MF-Millipore Membrane Filter, mixed cellulose esters

VMWP02500
Hydrophilic, 0.05 µm, 25 mm, white, plain, 100  
Retrieving price...
Price could not be retrieved
Minimum Quantity needs to be mulitiple of
Upon Order Completion More Information
You Saved ()
 
Request Pricing
Limited AvailabilityLimited Availability
In Stock 
Discontinued
Limited Quantities Available
Availability to be confirmed
    Remaining : Will advise
      Remaining : Will advise
      Will advise
      Contact Customer Service

       

      Contact Customer Service

      Click To Print This Page

      Overview

      Replacement Information

      Key Spec Table

      Description
      Catalogue NumberVMWP02500
      Trade Name
      • MF-Millipore
      DescriptionMF-Millipore Membrane Filter, mixed cellulose esters
      References
      Product Information
      Filter CodeVMWP
      Filter ColorWhite
      Maximum Operating Temperature75 °C
      Applications
      ApplicationThis 25 mm MF-Millipore membrane is composed of mixed cellulose membrane & has a 0.05 um pore size. With biologically inert mixtures of cellulose acetate & cellulose nitrate, MF-Millipore membranes are widely used in analytical/research applications.
      Biological Information
      MediaMF-Millipore
      WettabilityHydrophilic
      Physicochemical Information
      Refractive Index1.5
      Pore Size0.05 µm
      Air Flow Rate0.25 L/min x cm²
      Bubble Point at 23 °C≥17.6 bar, air with water
      Gravimetric Extractables1.5%
      Porosity %72%
      Water Flow Rate
      • 0.74 mL/min x cm²
      Dimensions
      Filter SurfacePlain
      Thickness100 µm
      Filter Diameter (⌀)25 mm
      Materials Information
      Chemistry
      • Mixed Cellulose Esters (MCE)
      Toxicological Information
      Safety Information according to GHS
      Safety Information
      Product Usage Statements
      Storage and Shipping Information
      Packaging Information
      Material SizeHydrophilic, 0.05 µm, 25 mm, white, plain, 100
      Transport Information
      Supplemental Information
      Specifications