Electrochemical degradation of nitrobenzene by anodic oxidation on the constructed TiO2-NTs/SnO2-Sb/PbO2 electrode.

Electrochemical degradation of nitrobenzene by anodic oxidation on the constructed TiO2-NTs/SnO2-Sb/PbO2 electrode.

Chemosphere (2014-07-30)

Yong Chen, Hongyi Li, Weijing Liu, Yong Tu, Yaohui Zhang, Weiqing Han, Lianjun Wang

ABSTRACT

The interlayer of Sb-doped SnO2 (SnO2-Sb) and TiO2 nanotubes (TiO2-NTs) on Ti has been introduced into the PbO2 electrode system with the aim to reveal the mechanism of enhanced electrochemical performance of TiO2-NTs/SnO2-Sb/PbO2 electrode. In contrast with the traditional Ti/SnO2-Sb/PbO2 electrode, the constructed PbO2 electrode has a more regular and compact morphology with better oriented crystals of lower size. The TiO2-NTs/SnO2-Sb interlayer prepared by electrodeposition process improves PbO2 coating structure effectively, and enhances the electrochemical performance of PbO2 electrode. Kinetic analyses indicated that the electrochemical oxidation of nitrobenzene on the PbO2 electrodes followed pseudo-first-order reaction, and mass transport was enhanced at the constructed electrode. The accumulation of nitrocompounds of degradation intermediates on constructed electrode was lower, and almost all of the nitro groups were eliminated from aromatic rings after 6h of electrolysis. Higher combustion efficiency was obtained on the constructed TiO2-NTs/SnO2-Sb/PbO2 electrode. The intermediates of nitrobenzene oxidation were confirmed by IC and GC/MS.

MATERIALS

Product Number

Brand

Product Description

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

695912

Sigma-Aldrich

Lead, shot, 1-3 mm, 99.995% trace metals basis

266035

Sigma-Aldrich

Titanium, wire, diam. 1.0 mm, 99.99% trace metals basis

369489

Sigma-Aldrich

Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis

248576

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, −325 mesh, ≥99% trace metals basis

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

396117

Sigma-Aldrich

Lead, shot, <2 mm, 99.9% trace metals basis

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

232033

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, 99.8% trace metals basis

348791

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, 99.7% trace metals basis

348848

Sigma-Aldrich

Titanium, foil, thickness 0.025 mm, 99.98% trace metals basis

391352

Sigma-Aldrich

Lead, powder, −100 mesh, 99.95% trace metals basis

305812

Sigma-Aldrich

Titanium, ≤10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

IRMM531B

Titanium, IRMM^®, certified reference material, 0.5 mm foil

IRMM531C

Titanium, IRMM^®, certified reference material, 0.5 mm wire

460400

Sigma-Aldrich

Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis

267902

Sigma-Aldrich

Titanium, wire, diam. 0.81 mm, 99.7% trace metals basis

GF52659940

Lead, foil, not light tested, 25x25mm, thickness 0.0125mm, 99.99+%

GF89377701

Titanium, tube, 100mm, outside diameter 25.4mm, inside diameter 23.62mm, wall thickness 0.89mm, annealed, 99.6+%

GF32801251

Titanium, tube, 1000mm, outside diameter 1.05mm, inside diameter 0.75mm, wall thickness 0.15mm, annealed, 99.6+%

GF82688709

Lead, foil, 25mm disks, thickness 0.25mm, as rolled, 99.95%

GF52551222

Titanium, microfoil, disks, 10mm, thinness 0.25μm, specific density 112.6μg/cm², permanent mylar 3.5μm support, 99.6+%

GF90963928

Titanium, rod, 25mm, diameter 50mm, 99.99+%

GF81436057

Titanium, rod, 500mm, diameter 4mm, annealed, 99.6+%

GF82517722

Titanium, tube, 1000mm, outside diameter 6.35mm, inside diameter 4.57mm, wall thickness 0.89mm, annealed, 99.6+%

GF98611623

Titanium, rod, 200mm, diameter 8.0mm, as drawn, 99.99+%

GF50171318

Titanium, rod, 25mm, diameter 16mm, as drawn, 99.99+%

GF03838282

Titanium, rod, 500mm, diameter 1.5mm, annealed, 99.6+%

GF72212813

Titanium, tube, 200mm, outside diameter 25.4mm, inside diameter 23.62mm, wall thickness 0.89mm, annealed, 99.6+%