1.05570
TLC Silica gel 60 F254
pkg of 25 sheets, sheet L × W 20 cm × 10 cm, aluminum support
ログインで組織・契約価格をご覧ください。
サイズを選択してください
表示を変更する
この商品について
NACRES:
NB.21
UNSPSC Code:
41115711
Feature:
binder Organic Polymer, fluorescent indicator
Particle size:
10-12 μm
Pore size:
60 Å medium pore diameter
Layer thickness:
200 μm
Plate l × w:
5 cm × 20 cm
Material:
aluminum support, silica gel 60 matrix
Quality Segment
material
aluminum support, silica gel 60 matrix
feature
binder Organic Polymer, fluorescent indicator
packaging
pkg of 25 sheets
technique(s)
thin layer chromatography (TLC): suitable
layer thickness
200 μm
plate L × W
5 cm × 20 cm
sheet L × W
20 cm × 10 cm
particle size
10-12 μm
pore size
60 Å medium pore diameter
storage temp.
2-30°C
General description
25 Aluminium sheets 10 x 20 cm
Our classical silica TLC plates are based on a combination of our proven silica gel 60 and the addition of a unique polymeric binder resulting in a very adherent and hard surface that will not crack or blister and even allow writing with a pensil on the surface without risk to damage the layer.
Application
- Nonstoichiometric Protic Ionic Liquids: The Role of Excess Acid in Charge Transport Mechanisms: This research examines the influence of trifluoromethanesulfonic acid in creating nonstoichiometric protic ionic liquids, providing a foundation for enhancing ionic conductivity and battery technologies (Middendorf and Schönhoff, 2024).
- B(9)-OH-o-Carboranes: Synthesis, Mechanism, and Property Exploration: The study explores the utilization of trifluoromethanesulfonic acid in the synthesis of boron-rich clusters, highlighting its role in the development of new materials with unique chemical properties (Ma et al., 2023).
- High pressure as a novel tool for the cationic ROP of γ-butyrolactone: Demonstrates trifluoromethanesulfonic acid′s application in polymer chemistry, specifically in ring-opening polymerization under high-pressure conditions, opening avenues for materials science research (Bernat et al., 2021).
- Peptide Cyclization Mediated by Metal-Free S-Arylation: This research utilizes trifluoromethanesulfonic acid to facilitate peptide cyclization, a crucial reaction in the development of therapeutic peptides and pharmaceutical applications (Kobayashi et al., 2021).
Analysis Note
Specific surface area (according to BET; 5-Pt. measurement): 480 - 540 m²/g
Pore volume (N₂-isotherm): 0.74 - 0.84 ml/g
d 50 (laser diffraction, size distribution): 9.5 - 11.5 µm
Layer thickness: 165 - 235 µm
Deviation of layer thickness per plate: ≤ 35 µm
Chromatographic testing:
colour test
hRf-values
- bleu vif organol, colour test, lipophile:
11 - 25
- Ceres Black G, colour test, lipophile: 34 - 48
- ceres Violet brn, colour test, lipophile: 52 - 67
Typical value determined on a conditioned sheet
Eluent: toluene (45% rel. humidity)
Pore volume (N₂-isotherm): 0.74 - 0.84 ml/g
d 50 (laser diffraction, size distribution): 9.5 - 11.5 µm
Layer thickness: 165 - 235 µm
Deviation of layer thickness per plate: ≤ 35 µm
Chromatographic testing:
colour test
hRf-values
- bleu vif organol, colour test, lipophile:
11 - 25
- Ceres Black G, colour test, lipophile: 34 - 48
- ceres Violet brn, colour test, lipophile: 52 - 67
Typical value determined on a conditioned sheet
Eluent: toluene (45% rel. humidity)
Still not finding the right product?
Explore all of our products under TLC Silica gel 60 F254
試験成績書（COA）
製品のロット番号・バッチ番号を入力して、試験成績書（COA） を検索できます。ロット番号・バッチ番号は、製品ラベルに「Lot」または「Batch」に続いて記載されています。